PROPERTY |
METHOD |
SI UNIT |
SI VALUE |
ENG. UNIT |
ENG. VALUE |
DENSITY |
ASTM D-792 |
Kg/m3 |
960 |
1bs/ft3 |
59.88 |
YIELD POINT |
ASTM D-638 |
MPa |
29.5 |
psi |
4279 |
ELONGATION AT YIELD |
ASTM D-638 |
% |
18 |
% |
18 |
TENSILE BREAK |
ASTM D-638 |
MPa |
30.5 |
psi |
4423 |
ELONGATION AT BREAK |
ASTM D-638 |
% |
1350 |
% |
1350 |
TENSILE MODULUS |
ASTM D-638 |
MPa |
1550 |
psi |
224812 |
FLEXURAL MODULUS |
ASTM D-790 |
MPa |
1150 |
psi |
166796 |
IZOD IMPACT |
ASTM D-4020 |
J/m |
67 |
ft-lbs/inch |
1.3 |
TENSILE IMPACT |
DIN 53448 |
kJ/m2 |
570 |
ft-lbs/inch2 |
570 |
HARDNESS |
ASTM D-2240 |
Type D |
67 |
Type D |
67 |
MELT POINT |
ASTM D-3417 |
ºC |
126-129 |
ºF |
259-267 |
COMPRESSIVE MODULUS |
ASTM D-621 |
MPa |
na |
Psi |
na |
COMPRESSIVE DEFORMATION |
ASTM D-621 |
% at 454.5 kg |
na |
% at 1000 psi |
na |
VOLUME RESISTIVITY |
ASTM D-257 |
Ohm-cm |
>1015 |
Ohm-cm |
>1015 |
SURFACE RESISTIVITY |
ASTM D-257 |
Ohm |
>1015 |
Ohm |
>1015 |
WATER ABSORPTION |
ASTM D-570 |
% |
slight |
% |
slight |